Page 391 - Slower hardener - Slower thinner - Higher processing viscosity - Higher dry coat thickness - Shorter drying times - Faster drying Lower gloss level: - Hardener with lower solid content - Faster hardener - Faster thinner - Lower processing viscosity - Lower dry coat thickness - Longer drying times - Air drying Base surfaces: - Standox(R) Basecoat - Standohyd(R) Basecoat NOTE: - Raw material base: Two-component acrylic resin - Flash point: 24° C/75.2° F - Spec. weight: 1.04 g/cm3 - Solid content: 51.3% weight/42.8% vol. - Theoretical yield: 7.8 m2/ltr. with a dry coat thickness of 50 microns - Clean equipment after use with cleaning thinner VOC value: - 505 g/l WARNING:  2K paints react with moisture. All work equipment, mixing vessels, etc. must therefore be completely water-free S 9.8.4.1 Processing